Graphite intercalation compounds are produced from the natural graphite flakes. Which are compressed into foils without binder or filler. Graphite sheets are manufactured in various forms, namely unreinforced, impregnated or reinforced. Absence of binders means no ageing or embrittlement. Long-term stability of compressibility and recovery over a wide temperature range. No cold or warm flow up to maximum permissible gasket stress. High creep strength under compressive stress. Properties highly anisotropic, particularly in respect of electrical and thermal conductivity. Resistance to radiation and thermal shock.

Flexiteck GS : Pure Graphite Sheet
Flexiteck GS-316T : Tanged AISI 316 Stainless Steel Sheet 0.10mm Thick
Flexiteck GS-316F : Foil AISI 316 Stainless Steel 0.10mm Thick or other Alloy Steel
Felxiteck GT : Corrugated Flexible Graphite Tape with one side adhesive
Flexiteck SS : Eyelet (SS) on ID & OD

Model 2300A: Pure Graphite Sheet
Model 2300B: Tanged AISI 316 Stainless Steel Sheet 0.10mm Thick
Model 2300C: Foil AISI 316 stainless Steel Sheet 0.10mm Thick
Or other Alloy Steel.
Model 2300D: Corrugated Flexible Graphite Tape with one side adhesive
Model 2300E : wire reinforced

TECHNICAL DATA  :

Carbon Content :                                                            > 98%
Sulphur Content :                                                           < 1500ppm
Chloride Content :                                                          < 50ppm
Fluoride Content :                                                          < 50ppm
Density :                                                                           1.0 ~ 1.6 gm/cm3
Gas permeability (DIN 3535) :                                     < = 0.6 ~ 1.0 cm3/min
ASTM “m” factor :                                                            2.5 ~ 3.0 psi
“y” stress :                                                                        4000 ~ 9000 psi
Deformation factors DIN 28090 T02
Compressibility :                 (E ksw)                              35 to 45 %    
Recovery :                           (E krw)                                 4 to 6 %
Young”s modulus (DIN 28090) :                                 950 N/mm2
Temperature (Inert atmosphere) :                               -200 ~ 1200 C
Pressure  :                                                                        102 Bar  ( 1480 psi )